ʻO Abrasive White Fused Alumina White Aluminum Oxide Powder no ka Polishing Blasting Lapping Grinding
Aʻo hou mai- Kūlana Huahana:Pauda keʻokeʻo
- Hōʻike:0.7 um-2.0 um
- ʻoʻoleʻa:2100kg/mm2
- Kaumaha Molekala:102
- Lae hehee:2010 ℃-2050 ℃
- Lae paila:2980 ℃
- Hiki ke hoʻoheheʻe wai:ʻAʻole hiki ke hoʻonā i ka wai
- ʻAiʻa:3.0-3.2g/cm3
- maʻiʻo:99.7%
-
ʻO ka hoʻomaloʻo a me ka wili ʻana i ka Micropowder Aluminum Oxide Powder no ka Sintering Corundum a me nā Ceramics
Aʻo hou mai- Kūlana Huahana:Pauda keʻokeʻo
- Hōʻike:0.7 um-2.0 um
- ʻoʻoleʻa:2100kg/mm2
- Kaumaha Molekala:102
- Lae hehee:2010 ℃-2050 ℃
- Lae paila:2980 ℃
- Hiki ke hoʻoheheʻe wai:ʻAʻole hiki ke hoʻonā i ka wai
- ʻAiʻa:3.0-3.2g/cm3
- maʻiʻo:99.7%
-
99.99% Maʻemaʻe Al2O3 Aluminum Oxide Pauka
Aʻo hou mai- Kūlana Huahana:Pauda keʻokeʻo
- Hōʻike:0.7 um-2.0 um
- ʻoʻoleʻa:2100kg/mm2
- Kaumaha Molekala:102
- Lae hehee:2010 ℃-2050 ℃
- Lae paila:2980 ℃
- Hiki ke hoʻoheheʻe wai:ʻAʻole hiki ke hoʻonā i ka wai
- ʻAiʻa:3.0-3.2g/cm3
- maʻiʻo:99.7%
-
Aluminum Oxide Polishing Powder No ka pale kelepona
Aʻo hou mai- Kūlana Huahana:Pauda keʻokeʻo
- Hōʻike:0.7 um-2.0 um
- ʻoʻoleʻa:2100kg/mm2
- Kaumaha Molekala:102
- Lae hehee:2010 ℃-2050 ℃
- Lae paila:2980 ℃
- Hiki ke hoʻoheheʻe wai:ʻAʻole hiki ke hoʻonā i ka wai
- ʻAiʻa:3.0-3.2g/cm3
- maʻiʻo:99.7%
-
Hoʻomaʻamaʻa Abrasive Grinding Media Aluminum Oxide Polishing Powder Al2O3
Aʻo hou mai- Kūlana Huahana:Pauda keʻokeʻo
- Hōʻike:0.7 um-2.0 um
- ʻoʻoleʻa:2100kg/mm2
- Kaumaha Molekala:102
- Lae hehee:2010 ℃-2050 ℃
- Lae paila:2980 ℃
- Hiki ke hoʻoheheʻe wai:ʻAʻole hiki ke hoʻonā i ka wai
- ʻAiʻa:3.0-3.2g/cm3
- maʻiʻo:99.7%
-
ʻO ka pauka alumina kiʻekiʻe kiʻekiʻe 99.99 alumini oxide no ka polishing
Aʻo hou mai- Kūlana Huahana:Pauda keʻokeʻo
- Hōʻike:0.3 um-2.0 um
- ʻoʻoleʻa:2100kg/mm2
- Kaumaha Molekala:102
- Lae hehee:2010 ℃-2050 ℃
- Lae paila:2980 ℃
- Hiki ke hoʻoheheʻe wai:ʻAʻole hiki ke hoʻonā i ka wai
- ʻAiʻa:3.0-3.2g/cm3
- maʻiʻo:99.7%